Disk White HT 98x10mm

Zirconia Disk Ceraman White HT

Advantages:

• Ideal for copings and bridges
• Superior strength and translucence
• Sandblasting under 2-2.5 bar with Al2O3 granulation 50μ
• It is recommended to glaze Ivoclar, Shofu or Vita structures

Chemical composition:

• ZrO2 + HfO2 + Y2O3: ≥99%
• Y2O3: 4.5% - 6%
• HfO2: ≤5%
• Al2O3: ≤0.5%
• Other oxides: ≤0.5%

 Physical properties:

• Density before sintering: 3.1±0.5 g/cm3
• Density after sintering: 6.07±0.01 g/cm3
• CTE (25-500°C): 10.5±1.0x10-6K-1
• 3-point flexural strength after sintering: 1400Mpa
• Translucency: 37%
• Chemical solubility after sintering: <100 ug/cm2
• Cytotoxicity test: level 0
• Radioactivity: <0.1Bg/g
• Sintering temperature: 1400-1550°C

 Indications:

• Coping: yes
• Structure: yes
• Total bridges (Less than 3 sequential pntics for the anterior, less than 2 sequential pontics for the posterior): yes
• Cantilever bridge (Except the patient with bruxism): yes
• Inlay bridge (Except the patient with bruxism): yes
• Marylabd bridge (Except the patient with bruxism): yes
• Telescopic crown: yes
• Custom implants: yes