Disk White HT 98x14mm
€69
Tax included
Zirconia Disk Ceraman White HT
Advantages:
- Ideal for copings and bridges
- Superior strength and translucence
- Sandblasting under 2-2.5 bar with Al2O3 granulation 50μ
- It is recommended to glaze Ivoclar, Shofu or Vita structures
Chemical composition:
- ZrO2 + HfO2 + Y2O3: ≥99%
- Y2O3: 4.5% - 6%
- HfO2: ≤5%
- Al2O3: ≤0.5%
- Other oxides: ≤0.5%
Physical properties:
- Density before sintering: 3.1±0.5 g/cm3
- Density after sintering: 6.07±0.01 g/cm3
- CTE (25-500°C): 10.5±1.0x10-6K-1
- 3-point flexural strength after sintering: 1400Mpa
- Translucency: 37%
- Chemical solubility after sintering: <100 ug/cm2
- Cytotoxicity test: level 0
- Radioactivity: <0.1Bg/g
- Sintering temperature: 1400-1550°C
Indications:
- Coping: yes
- Structure: yes
- Total bridges (Less than 3 sequential pntics for the anterior, less than 2 sequential pontics for the posterior): yes
- Cantilever bridge (Except the patient with bruxism): yes
- Inlay bridge (Except the patient with bruxism): yes
- Marylabd bridge (Except the patient with bruxism): yes
- Telescopic crown: yes
- Custom implants: yes
Delivery form:
- Zirconia Disk Ceraman White HT- 1 piece