Disk 3D Multilayer 98x14mm
€206
Tax included
Zirconia Disk Multilayer 3D - Color, transparency and natural hardness
Advantages:
- 6 natural shade layers that match the natural tooth, from the cervical to incisal area
- Gradual translucency - from 57% in the incisal area to 43% in the cervical area
- Thanks to the gradual translucency, it is possible to obtain an enamel translucency similar to natural tooth
- Low translucency in the cervical area allows an opaque effect
- Gradual hardness from 600 Mpa to 900 Mpa
Composition and chemical characteristics:
- Y2O3: 9.28wt%
- Al2O3: 0.05wt%
- SiO2: ≤0.002wt%
- Fe2O3: ≤0.15wt%
- Co3O4: ≤0.02wt%
- Chemical solubility: ≤2000u g.cm-2
Mechanical properties:
- Sintering density: ≥6.0g/cm3
- Fracture resistance: 5Mpam½
- Hardness (Hv10): 1250
Flexural strength:
- Strength layer 1 (thickness 20%): >600MPa
- Strength layer 2 (thickness 15%): >660MPa
- Strength layer 3 (thickness 15%): >730MPa
- Strength layer 4 (thickness 15%): >780MPa
- Strength layer 5 (thickness 15%): >830MPa
- Strength layer 6 (thickness 20%): >900MPa
Delivery form:
- Zirconia Disk Multilayer 3D - 1 piece