Disk White TT 98x16mm

Zirconia Disk White Ceraman TT

Advantages:

• Suitable for anterior restoration
• Superior glassy translucency and strength
• Short tooth preparation time
• Sandblasting under 2-2.5 bar with Al2O3 granulation 50μ
• It is recommended to glaze Ivoclar, Shofu or Vita structures

Chemical composition: 

• ZrO2 + HfO2: 86.3% - 94.2%
• Y2O3: 5.8% - 9.7%
• Er2O3: <2%
• Fe2O3: <0.5%
• Al2O3: ≤0.5%
• Other oxides: ≤0.5%

Physical properties:

• Density before sintering: > 2.8g/cm3   
• Density after sintering: 6.04 g/cm3   
• CTE (25-500°C): 10.5±1.0x10-6K-1
• 3-point flexural strength after sintering: >600Mpa
• Translucency: 49%
• Chemical solubility after sintering: <100ug/cm2
• Cytotoxicity test: level 0
• Radioactivity after sintering: <0.1Bg/g
• Sintering temperature: 1430-1470°C

Indications:

• Crowns: yes
• 2-4 unit Bridges: yes
• Implants: yes
• Telescopic crown: yes
• Veneer (Except the patient with bruxism): yes

Delivery form:

• Zirconia Disk White Ceraman TT - 1 piece