Disk TT-Multilayer 98x14mm
€131
Tax included
Zirconia Disk Ceraman TT-Multilayer
Advantages:
- Ideal for for anterior restoration
- Natural tooth appearance
- No coloring needed
- Sandblasting under 2-2.5 bar with Al2O3 granulation 50μ
- It is recommended to glaze Ivoclar, Shofu or Vita structures
Chemical composition:
- ZrO2 + HfO2: 86.3% - 94.2%
- Y2O3: 5.8% - 9.7%
- Fe2O3: <2%
- Er2O3: < 0.5%
- Al2O3: < 0.5%
- Other oxides: ≤0.5%
Physical properties:
- Density before sintering: >2.8 g/cm3
- Density after sintering: ≥6.0 g/cm3
- CTE (25-500°C): (10.5 ± 1.0) × 10-6k-1
- 3-point flexural strength after sintering: >600 Mpa
- Chemical solubility after sintering: <100 Bg/g
- Cytotoxicity test: level 0
- Radioactivity: <0.1Bg/g
- Translucency: 49%
- Sintering temperature: 1430-1470°C
Indications:
- Crown: yes
- 2-4 unit Bridges: yes
- Telescopic crown: yes
- Veneer (Except the patient with bruxism): yes
Delivery form:
- Zirconia Disk TT-Multilayer Ceraman - 1 piece