Disk TT-Multilayer 98x20mm

Zirconia Disk Ceraman TT-Multilayer

Advantages:

• Ideal for for anterior restoration
• Natural tooth appearance
• No coloring needed
• Sandblasting under 2-2.5 bar with Al2O3 granulation 50μ
• It is recommended to glaze Ivoclar, Shofu or Vita structures

Chemical composition:

• ZrO2 + HfO2: 86.3% - 94.2%
• Y2O3: 5.8% - 9.7%
• Fe2O3: <2%
• Er2O3: < 0.5%
• Al2O3: < 0.5%
• Other oxides: ≤0.5%

Physical properties:

• Density before sintering: >2.8 g/cm3
• Density after sintering: ≥6.0 g/cm3
• CTE (25-500°C): (10.5 ± 1.0) × 10-6k-1
• 3-point flexural strength after sintering: >600 Mpa
• Chemical solubility after sintering: <100 Bg/g
• Cytotoxicity test: level 0
• Radioactivity: <0.1Bg/g
• Translucency: 49%
• Sintering temperature: 1430-1470°C

Indications:

• Crown: yes
• 2-4 unit Bridges: yes
• Telescopic crown: yes
• Veneer (Except the patient with bruxism): yes

Delivery form:

• Zirconia Disk Ceraman TT-Multilayer - 1 piece